Material Resilience Engine
Public demoNot certifiedOriginal alloy
UNS R30075 (ASTM F75) Co-Cr-Mo Alloy
Cobalt-chromium-molybdenum alloy
Use case
Fatigue critical
Production method
Any route
Targets
2,781
Candidates
10,746
Source
Supabase
Material records
50,163
Unique materials
4,836
Compositions
3,206
Evidence links
30,671
Scenarios
6
Published bundle
30 files
Mechanical property gate
| Property | Target | Candidate range | Gate |
|---|---|---|---|
| Yield strength | 480 MPa | 573 to 1118 MPa | candidate overlap |
| Ultimate tensile strength | 780 MPa | 992 to 1415 MPa | candidate overlap |
| Fatigue strength | 250 MPa | 227 to 259 MPa | close match |
| Elongation | 12% | 14 to 16% | candidate overlap |
| Density | 8.4 g/cm3 | 7.93 to 8.44 g/cm3 | close match |
Material Resilience Engine
Public demoNot certifiedOriginal alloy
UNS R30075 (ASTM F75) Co-Cr-Mo Alloy
Cobalt-chromium-molybdenum alloy
Use case
Fatigue critical
Production method
Any route
Targets
2,781
Candidates
10,746
Source
Supabase
Material records
50,163
Unique materials
4,836
Compositions
3,206
Evidence links
30,671
Scenarios
6
Published bundle
30 files
Mechanical property gate
| Property | Target | Candidate range | Gate |
|---|---|---|---|
| Yield strength | 480 MPa | 573 to 1118 MPa | candidate overlap |
| Ultimate tensile strength | 780 MPa | 992 to 1415 MPa | candidate overlap |
| Fatigue strength | 250 MPa | 227 to 259 MPa | close match |
| Elongation | 12% | 14 to 16% | candidate overlap |
| Density | 8.4 g/cm3 | 7.93 to 8.44 g/cm3 | close match |